PEMBUATAN PULP DAN KERTAS BERBASIS SERAT SAGU MENGGUNAKAN PROSES SODA UNTUK APLIKASI PEMBUATAN KEMASAN

Experiment on the manufacture of pulp and paper made from sagu fiber has been conducted. The manufacture of pulp and paper was carried out using the sulfate chemical method with a mixture of 160 grams of NaOH solution then mixed with 3200 ml of water cooked using a rotary digester machine for 4 hours at a temperature of 1700 C. The ratio of the sample to the cooking solution was 1:4. After cooking, the pulp was dried and dried with a centrifuge machine. Before molding, the pulp was ground to obtain the degree of fineness. The ideal pulp grade is 250 - 500 ml. After that, the pulp is molded to obtain paper sheets. The results of testing the physical properties of sagu fiber-based paper obtained basic weight, paper thickness, oil absorption, tear resistance, moisture content, and pH with an average of 49.40 g/m2; 13.46 µm; 90.525 1000/mm; 153.15 mN; in pH testing obtained an average result of 6.

Experiment tentang Pembuatan pulp dan kertas yang terbuat dari serat sagu telah dilakukan. Pembuatan pulp dan kertas dilakukan dengan menggunakan metode kimia sulfat dengan campuran larutan NaOH sebanyak 160 gram lalu dicampurkan dengan air sebanyak 3200 ml dimasak dengan menggunakan mesin rotary digester selama 4 jam dengan suhu 1700 C. Perbandingan sampel dengan larutan pemasak 1:4. Setelah dimasak, pulp dikeringkan dan dikeringkan dengan mesin centrifuge. Sebelum dicetak pulp digiling terdahulu untuk mendapatkan derajat kehalusan. Nilai ideal pulp yaitu 250 – 500 ml. Setelah itu pulp dicetak hingga mendapatkan lembaran kertas. Hasil pengujian sifat fisis kertas berbasis serat sagu didapat berat dasar, ketebalan kertas, daya serap minyak, ketahanan sobek, kadar air, dan pH dengan rata-rata sebesar 49,40 g/m2; 13,46 µm; 90,525 1000/mm; 153,15 mN; pada pengujian pH mendapatkan hasil rata-rata sebesar 6.