KARAKTERISASI KUALITAS VISUAL DAN KETAHANAN FISIK OVERPRINT VARNISH BERBASIS MINYAK MINERAL DAN PALM OIL

ABSTRACT
Overprint Varnish (OPV) is a transparent protective coating applied to the surface of printed materials to enhance their visual quality and physical durability. One of the products developed by PT Sakata Inx Indonesia is OPV, which is available in both mineral oil-based and non-mineral oil-based formulations. This study aims to determine the visual quality and physical durability characteristics of mineral oil-based and non-mineral-based OPV when applied to coated and uncoated paper substrates. The mineral oil-based OPV was obtained from PT Sakata Inx Indonesia, while the non-mineral formulation used palm oil. Quality testing was conducted based on two aspects: visual quality, which included CIE L*a*b and gloss testing; and physical durability, which included scratch resistance and Coefficient of Friction (CoF) testing. The test results show that mineral oil-based and non-mineral oil-based OPVs have relatively similar visual quality characteristics in terms of CIE L*a*b values, with only minor differences in color tendency. Meanwhile, regarding gloss values, abrasion resistance, and the coefficient of friction based on the test results, non-mineral-oil materials have the potential to be used as alternative raw materials for OPV while maintaining visual quality and physical durability.

ABSTRAK
Overprint Varnish (OPV) merupakan lapisan pelindung transparan yang diaplikasikan pada permukaan cetakan dalam meningkatkan kualitas visual maupun ketahanan fisik cetakan. Salah satu produk yang dikembangkan di PT Sakata Inx Indonesia adalah OPV, baik yang berbasis mineral maupun minyak non-mineral. Penelitian ini bertujuan untuk mengetahui karakteristik kualitas visual dan ketahanan fisik OPV berbasis minyak mineral dan palm oil yang diaplikasikan pada substrat coated paper dan uncoated paper. OPV yang diformulasikan menggunakan minyak mineral PT Sakata Inx Indonesia, sedangkan pada minyak non-mineral penulis menggunakan palm oil. Pengujian kualitas dilakukan berdasarkan dua aspek, yaitu kualitas visual yang meliputi pengujian CIE L*a*b dan gloss, serta ketahanan fisik yang meliputi pengujian rub resistance dan coefficient of friction (CoF). Hasil pengujian menunjukkan bahwa OPV berbasis minyak mineral dan palm oil memiliki karakteristik kualitas visual yang relatif serupa pada nilai CIE L*a*b, dengan perbedaan kecil pada kecenderungan warna. Sedangkan pada nilai gloss, skala tergosok, dan koefisien friksi berdasarkan hasil penulisan menunjukkan bahwa palm oil berpotensi digunakan sebagai alternatif bahan baku OPV dengan tetap mempertahankan kualitas visual dan ketahanan fisik.