PERBANDINGAN KOMPOSISI SOLVENT NPA DAN NPAC PADA TINTA FLEXO SOLVENT-BASED TERHADAP KUALITAS CETAK SUBSTRATE BOPP

Penelitian ini bertujuan untuk menganalisis pengaruh komposisi solvent
terhadap kualitas cetak pada substrate BOPP menggunakan tinta flexo berbasis
solvent. Solvent yang diuji adalah NPA (Normal Propyl Alcohol) dan NPAC (Normal
Propyl Acetate), yang masing-masing memiliki karakteristik titik didih dan
polaritas berbeda. Metode yang digunakan dalam penelitian ini adalah eksperimen
laboratorium di fasilitas PT Siegwerk Indonesia. Proses pencetakan dilakukan
menggunakan mesin RK Flexiproof, sedangkan parameter kualitas cetak yang
dievaluasi meliputi boiling point, gloss, adhesion, density, dan opacity. Pengujian
gloss dilakukan dengan glossmeter, sedangkan density dan opacity diuji
menggunakan densitometer X-Rite. Adhesion diuji menggunakan metode tape test
standar industri. Komposisi tinta disiapkan dalam volume 200gram dengan rasio
pelarut 1:1. Hasil penelitian menunjukkan bahwa solvent NPAC lebih unggul dalam
menghasilkan gloss tinggi, sedangkan NPA lebih baik dalam aspek adhesion,
density, dan opacity. Temuan ini diharapkan dapat memberikan kontribusi terhadap
optimalisasi formulasi tinta fleksografi yang sesuai untuk aplikasi pada substrate
film BOPP dalam industri kemasan.
Kata Kunci: tinta flexo, solvent, kualitas cetak, BOPP, fleksografi.

This study aims to analyze the effect of solvent composition on print quality
on BOPP substrates using solvent-based flexographic inks. The solvents tested were
NPA (Normal Propyl Alcohol) and NPAC (Normal Propyl Acetate), each of which
has different point characteristics and polarity. The method used in this study was
a laboratory experiment at PT Siegwerk Indonesia's facilities. The printing process
was carried out using an RK Flexiproof machine, while the print quality parameters
evaluated included boiling point, gloss, adhesion, density, and opacity. Gloss
testing was performed with a glossmeter, while density and opacity were tested
using an X-Rite densitometer. Adhesion was tested using the industry-standard tape
test method. The ink composition was prepared in a 200-gram volume with a 1:1
solvent ratio. The results showed that NPAC solvent was superior in producing high
gloss, while NPA was superior in adhesion, density, and opacity. These findings are
expected to contribute to the optimization of flexographic ink formulations suitable
for application on BOPP film substrates in the packaging industry.
Keywords: flexo ink, solvent, print quality, BOPP, flexography.