PENGUJIAN KUALITAS COATING NITROCELLULOSE PADA SUBSTRAT KERTAS OPACITY CHART

ABSTRACT
This study aims to analyze the effect of viscosity on the quality of nitrocellulose coatings applied to Opacity Chart paper substrates, evaluating parameters such as
gloss, opacity (hiding power), and coating uniformity.Testing was conducted at PT Siegwerk Indonesia using three types of nitrocellulose—NC 1/4, NC 1/8, and NC
1/16—subjected to three treatment variations: original, 10% reduction, and 20% reduction. An experimental method with a quantitative descriptive approach was employed. Viscosity was measured using a Zahn Cup No. 2, coatings were applied using a bar coater, and gloss was measured using a glossmeter. The results indicate that changes in viscosity significantly affect coating quality. Excessively high viscosity results in a coating that is difficult to level, thereby reducing surface uniformity, whereas excessively low viscosity leads to a coating that is too thin, resulting in reduced opacity. Based on the test results, samples with a 10% viscosity reduction across all nitrocellulose types achieved the best balance between gloss, opacity, and coating uniformity. This study demonstrates that viscosity control is a crucial factor in achieving optimal coating quality on Opacity Chart paper substrates. The findings are expected to serve as a reference for determining
appropriate viscosity ranges to enhance process consistency and product quality within the printing and packaging industries.
Keywords: Viscosity, Nitrocellulose, Coating, Gloss, Hiding power, Opacity chart

ABSTRAK
Pengujian ini bertujuan untuk menganalisis pengaruh viskositas terhadap kualitas coating nitrocellulose pada substrat kertas Opacity Chart berdasarkan parameter
gloss, daya tutup, dan keseragaman lapisan coating. Pengujian dilaksanakan di PT Siegwerk Indonesia menggunakan tiga jenis nitrocellulose, yaitu NC 1/4, NC 1/8,
dan NC 1/16, dengan tiga variasi perlakuan, yaitu original,reduce 10%, dan reduce 20%. Metode pengujian yang digunakan adalah metode eksperimen dengan
pendekatan deskriptif kuantitatif. Pengujian viskositas dilakukan menggunakan Zahn Cup No. 2, aplikasi coating menggunakan Barcoater, sedangkan pengukuran
gloss dilakukan menggunakan Glossmeter. Hasil pengujian menunjukkan bahwa perubahan viskositas berpengaruh terhadap kualitas lapisan coating. Viskositas yang terlalu tinggi menghasilkan lapisan yang sulit diratakan sehingga keseragaman permukaan menurun, sedangkan viskositas yang terlalu rendah menyebabkan lapisan coating menjadi terlalu tipis dan daya tutup berkurang. Berdasarkan hasil pengujian, sampel dengan kondisi reduce 10% pada masing-masing jenis nitrocellulose menghasilkan keseimbangan terbaik antara nilai gloss, daya tutup, dan keseragaman lapisan. pengujian ini menunjukkan bahwa pengendalian viskositas merupakan faktor penting dalam memperoleh kualitas coating yang optimal pada substrat kertas Opacity Chart. Hasil pengujian diharapkan dapat menjadi referensi dalam menentukan rentang viskositas yang sesuai untuk meningkatkan konsistensi proses coating serta kualitas produk pada industri percetakan dan kemasan.
Kata kunci: Viskositas, Nitrocellulose, Coating, Gloss, Daya tutup, Opacity
Chart